Delamination
I have made my first 132 layer Damascus knife blank made out of 1084 & 1520. On one side there looks to be a few cracks but none on the other side or edges. They didn’t show up until after normalization. I like to grind my blades after heat treat. I want to try to grind out the cracks / delaminations. Could heat treating cause more problems trying to grind out the cracks or make them worse? I would have posted a picture but had trouble uploading it. Thanks for any advise!
|
| Tags |
| 1084, art, blades, damascus, damascus knife, forging, grind, grinding, heat, heat treat, heat treating, hidden, knife, knife blank, made, make, post, question, show, steel |
| Currently Active Users Viewing This Thread: 1 (0 members and 1 guests) | |
|
|
Similar Threads
|
||||
| Thread | Thread Starter | Forum | Replies | Last Post |
| billet edge delamination | Mark Merz | Ed Caffrey's Workshop | 3 | 01-03-2003 07:44 PM |
Threaded Mode