Thanks for the info Ed. I was hoping that someone else had seen this before. I could not figure what I could have done to get a crack embedded within the blade.
I can understand your hesitation in wanting to use 5160. This is my first occurance like this, and I am considering not using it any more. The problem is that I still have quite a bit of it so I guess I will take my chances.
Thanks again
Brian
|