  #1  
Old 05-04-2019, 04:34 PM
Andrew Garrett's Avatar
Andrew Garrett Andrew Garrett is offline
Moderator
 
Join Date: Jun 2005
Location: Nampa, Idaho
Posts: 3,584
Cast Iron Knife

I'm pretty sure I just made a knife from cast iron.
I aquired an old Fairbanks Morse & Co double open-end wrench--most likely a 1920s vintage.
I hammered it out, ground it, heat treated it, finish ground it, and etched it. It felt like I was working tool steel the whole time, but the etched finish looks different than I expected.
It hardened fine--easily passing the file test.
I know they made cast iron wrenches a century ago, so I'm fairly convinced that's what I have here.

I just made a brittle knife, didn't I?
Attached Images
File Type: jpg castiron2.jpg (32.4 KB, 15 views)


__________________
Andy Garrett
https://www.facebook.com/GarrettKnives?ref=hl
Charter Member - Kansas Custom Knifemaker's Association
www.kansasknives.org

"Drawing your knife from its sheath and using it in the presence of others should be an event complete with oos, ahhs, and questions."

Last edited by Andrew Garrett; 05-04-2019 at 05:25 PM.
Reply With Quote
  #2  
Old 05-04-2019, 06:17 PM
Andrew Garrett's Avatar
Andrew Garrett Andrew Garrett is offline
Moderator
 
Join Date: Jun 2005
Location: Nampa, Idaho
Posts: 3,584
Ok. I worked it out.
I called my buddy Steve Culver ABS-MS, and we talked about it. I sent him some pics and it was decided that it could not be cast iron, as cast iron cannot ne forged--it would just crumble. Furthermore, it wouldn't make a good wrench. However, it does have a random grain structure without the linear properties of rolled foundery steel.
Since it heat-treated the same as most other simple carbon steels I've used, we concluded (he concluded--I agreed) that it is cast steel.
I may even get a bit of a dendritic edge when I sharpen it--just guessing on that one.


__________________
Andy Garrett
https://www.facebook.com/GarrettKnives?ref=hl
Charter Member - Kansas Custom Knifemaker's Association
www.kansasknives.org

"Drawing your knife from its sheath and using it in the presence of others should be an event complete with oos, ahhs, and questions."
Reply With Quote
  #3  
Old 05-04-2019, 06:18 PM
Doug Lester Doug Lester is offline
Hall of Famer
 
Join Date: Sep 2006
Location: Decatur, IL
Posts: 2,612
Doubtful. Cast iron does not forge all that well from what I understand.

Doug


__________________
If you're not making mistakes then you're not trying hard enough
Reply With Quote
  #4  
Old 05-04-2019, 10:52 PM
jimmontg jimmontg is offline
Guru
 
Join Date: Jan 2016
Location: Now live in Las Cruces NM.
Posts: 1,345
Cast Iron is misnamed.

Cast steel would be a better term. In my old job as a T.I.G. welder and welding all kinds of cast steels I can tell you the carbon content varies quite a bit, but if the cast iron is running .50 to .70% it will forge just fine and many old tools were made of cast steel in that range. Higher carbon is the stuff you can't forge and if you break one of those high carbon castings note how large the grain is on some of them. No kidding some castings were 4% carbon, impossible to weld.

I have welded pure cast iron and it welds like regular low carbon steel. It's the doggone carbon that causes problems. Your typical exhaust manifold is 2% carbon and welding it is nigh on next to impossible, so we'd use Ni-rod or nickel or silicon bronze to braze cracks. If you preheat it to 1200 degrees and slow cool it you can weld it, but almost nobody does that.
Reply With Quote
  #5  
Old 05-11-2019, 09:44 PM
Andrew Garrett's Avatar
Andrew Garrett Andrew Garrett is offline
Moderator
 
Join Date: Jun 2005
Location: Nampa, Idaho
Posts: 3,584
I put an edge on it and did the brass rod test all along the edge.
It's good.

Very happy with the blade. I hope to find some more such tools. Love the pattern when etched! Very 'wootz' like.


__________________
Andy Garrett
https://www.facebook.com/GarrettKnives?ref=hl
Charter Member - Kansas Custom Knifemaker's Association
www.kansasknives.org

"Drawing your knife from its sheath and using it in the presence of others should be an event complete with oos, ahhs, and questions."
Reply With Quote
Reply

Tags
abs, blade, brass, carbon, dendritic, edge, etched, file, finish, forge, forged, heat, iron, knife, made, make, old tools, simple, steel, tool, tool steel, vintage, wrench


Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
 
Thread Tools
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump

Similar Threads
Thread Thread Starter Forum Replies Last Post
Cast Blades? Andrew Garrett High-Performance Blades 1 04-06-2016 06:56 PM
cast iron question chipwit Heat Treating and Metallurgy 2 10-15-2004 10:14 AM
forging cast iron pipe DragonFang The Newbies Arena 2 04-20-2004 06:26 AM
Cast-on guards? WinDancer Tool Time 8 08-07-2003 10:04 AM
LIVE WEB CAST ALERT -- The Spirit of Steel Knife Show greg77630 Member Web Sites : Links & Updates 1 09-26-2001 05:09 AM


All times are GMT -5. The time now is 03:24 AM.




KNIFENETWORK.COM
Copyright © 2000
? CKK Industries, Inc. ? All Rights Reserved
Powered by ...

Powered by vBulletin® Version 3.8.4
Copyright ©2000 - 2024, Jelsoft Enterprises Ltd.
The Knife Network : All Rights Reserved