MEMBER ITEMS FOR SALE
Custom Knives | Other Knives | General Items
-------------------------------------------
New Posts | New PhotosAll Photos



Go Back   The Knife Network Forums : Knife Making Discussions > Custom Knife Discussion Boards > Ed Caffrey's Workshop

Ed Caffrey's Workshop Talk to Ed Caffrey ... The Montana Bladesmith! Tips, tricks and more from an ABS Mastersmith.

Reply
 
Thread Tools Display Modes
  #1  
Old 08-29-2004, 08:59 AM
Ed Caffrey's Avatar
Ed Caffrey Ed Caffrey is offline
Super Moderator
 
Join Date: Jun 2002
Location: Great Falls, Montana, USA
Posts: 4,147
Send a message via AIM to Ed Caffrey Send a message via Yahoo to Ed Caffrey
Your mehtods for cryo treating..gathering data

I had an interesting conversation yesterday, concerning cryo-treating blades. The methods used by the individual I was talking with at first seemed odd, but the more I thought about it, the more sense he made. Anyway, it made me think about the various methods that we use, so I thought I would ask a couple of questions to everyone here.

First, at what point do you cryo-treat your blades? What are your thoughts of the duration required for cryo-treating? (time) And, do you cryo-treat a specific blade more than one time?

For 52100 my method is to multiple harden the blade, conduct a "snap" temper, and then go into the cryo. Duration wise, I go for 6-8 hours in the cryo, and allow the blade to warm slowly back to room temp by placing the blade(s) between two layers of ka-wool. I follow this up with a triple temper, and then complete the knife.

So, don't be bashful........what methods to you use for cryo-treating your blades?


__________________

www.caffreyknives.net
EdCaffreyMS@caffreyknives.net
"Nobody cares what you know.....until they know you care."
See me at table 2Q at the Blade Show!
Reply With Quote
  #2  
Old 09-01-2004, 04:07 PM
Michael E. Mill Michael E. Mill is offline
Registered User
 
Join Date: Feb 2004
Location: Chandler, Oklahoma
Posts: 145
crogenics

When I do my own cable and layered damascus, I double temper then cryo then temper one more time. Most of the time I have 5 or 6 blades together and when cryoed do it for at least 6 hours and most of the time I put them in in the evening and return the next morning to get them out. I use a friendly farmers semen tank of liquid nirtrogen suspend them with stainless welding rod thru holes in the tang and suspend them slowlyuntil submerged. On my stock removal blades of D2 and ATS 34 I cryo them after they come back from a commercial heat treater and then temper them at 300 degrees for two hours. I have taken several of my knife store friends blades from commercial knives out and simply submerged them for the time period and they are amazed on the increased edge retention even if the factory says they are cryoed. I wonder then about the length of time they do them. For me at least 6 hours on everything and most end up 12 hours AND I FIRMLY BELIEVE IT HELPS. Mike
Reply With Quote
  #3  
Old 09-10-2004, 05:25 PM
mete's Avatar
mete mete is offline
Master
 
Join Date: Sep 2004
Location: NY State
Posts: 777
The problem with tempering and cryo is that tempering stabilizes the retained austenite preventing it from being transformed to martensite. There is some danger in going directly from quench to cryo as far as cracking so some will 'snap temper' but that must be done at a fairly low temperature such as 300F.Higher temperatures such as 400F will definitely stabilize the austenite.My suggestion would be to quench, snap temper at 300F for 1 hour , cryo,10 hours would be more than enough, then double temper.
Reply With Quote
  #4  
Old 09-19-2004, 10:03 AM
canyonman canyonman is offline
Enthusiast
 
Join Date: Mar 2003
Location: Culver Or
Posts: 73
Since I do most of my work(stock removal, 1095)on the weekends, I harden then a quick temper of 30 mins. @ 325F then I put it in my home freezer for a week or longer.
My question is do any of you think I'm doing any good or is this just a safe way of storing unfinished projects?

Larry
Reply With Quote
  #5  
Old 09-20-2004, 06:42 PM
Quenchcrack Quenchcrack is offline
Steel Addict
 
Join Date: Jun 2004
Location: NW Tennessee
Posts: 167
Cryo in the freezer

To put it into perspective, most high carbon steels achieve about 90% martensite when quenched down to room temperature. To get the other 10% you must cryo treat it. There is a somewhat linear relationship between the temperature at which you freeze it and the amount of martensite formed. LN is about -300F and your home freezer is about +32F. If you quench to say, 70F, there is a total of 370 degrees you need to get below. If you only freeze down 70-32 = 38 degrees, you have gone 38/370 or 10% of the remaining 10% or about a 1% improvement. Modest but better than a poke in the eye with a pointy stick.

Let me add my firm agreement with the comments regarding tempering and cryo treating. Austenite at room temperature is metastable; it does not want to be there! Tempering will cause the retained austenite to decompose to bainite or even pearlite. Once it has transformed, the cryo is not doing much. Quench it, snap draw it at 250F-300F for about 1/2 hr, cryo and retemper at your normal temperature.


__________________
Which is worse; ignorance or apathy? Who knows? Who cares?
Reply With Quote
  #6  
Old 09-20-2004, 09:41 PM
AwP AwP is offline
Master
 
Join Date: Mar 2004
Location: Cleveland, OH
Posts: 774
I haven't done any cryo yet, though now that I read that even a home freezer can have a slight effect I might have to start thinking about it a little more. I did have a couple questions though...

Quote:
Tempering will cause the retained austenite to decompose to bainite or even pearlite.
Is there a way to force the retained austenite to bainite and be sure not to get pearlite without marquenching and making the whole thing bainite? I'm thinking a mix of martinsite and bainite might not be a bad thing on a heavy duty chopper.

Quote:
The methods used by the individual I was talking with at first seemed odd, but the more I thought about it, the more sense he made.
Just purely being nosey, but what is this persons unusual method?


__________________
~Andrew W. "NT Cough'n Monkey" Petkus
Reply With Quote
  #7  
Old 09-21-2004, 12:55 PM
mete's Avatar
mete mete is offline
Master
 
Join Date: Sep 2004
Location: NY State
Posts: 777
I hope your home freezers are colder than +32F because the colder it is the longer you can keep food .It should be no warmer than +10F and preferably -10F. However even if it's -10F the influence on heat treating will be minor......AwP, you're confusing terms .Austempering gives you bainite. Marquenching or martempering gives you martensite.Typically the retained austenite will decompose to martensite at typical tempering temperatures [ below Ms ] I wouldn' try to produce duplex structures.... Also I should mention here that excessive austenitizing temperature will produce excessive retained austenite .
Reply With Quote
  #8  
Old 09-21-2004, 01:51 PM
AwP AwP is offline
Master
 
Join Date: Mar 2004
Location: Cleveland, OH
Posts: 774
Quote:
Austempering gives you bainite. Marquenching or martempering gives you martensite.Typically the retained austenite will decompose to martensite at typical tempering temperatures [ below Ms ] I wouldn' try to produce duplex structures....
Oops, austempering, I do get those two terms confused alot. So mixing martinsite and bainite isn't really something that'd be possible with a hope setup? Or is it that it's not as desirable as my armchair theory makes it seem like it would be?


__________________
~Andrew W. "NT Cough'n Monkey" Petkus
Reply With Quote
  #9  
Old 03-13-2017, 01:08 PM
Blade-Runner Blade-Runner is offline
 
Join Date: Mar 2017
Location: North York
Posts: 2
Hi Everyone!

I am fairly new to the knife making world, and extremely interested in performing a cryogenic treatment on my knives to really improve their performance. However, there doesn't seem to be a whole lot of companies building smaller machines out there. With some searching, I found one place that builds smaller machines for around $6k US, which was by far the best I came across. However, I am curious if anyone out there has any suggestions on where to get a machine, or of any respectable companies that build smaller machines to fit a custom knife makers size, and of course, our budget?
Reply With Quote
  #10  
Old 03-13-2017, 01:37 PM
mr.HC mr.HC is offline
Enthusiast
 
Join Date: Jan 2017
Location: Saukville, WI
Posts: 64
austa, bainta, marqta, you guys lost me right from the start, could someone please speak English so I can follow along lol

Carl
Reply With Quote
  #11  
Old 03-13-2017, 11:51 PM
jimmontg jimmontg is online now
Skilled
 
Join Date: Jan 2016
Location: Mountains of Western NC.
Posts: 700
13 year old thread.
Blade Runner what type of a machine are you talking about for doing cryo? For $6000 I can buy you a 24" deep Paragon oven and a $300 dewar for holding liquid nitrogen. Plus build you a dry ice freezer for metals like AEB-L which only cryo at -95F and dry ice is -109F. AeB-L is a great knife steel and one of the easier stainless to HT into knives. After all that still have $2000 leftover, are you talking about a deep freeze freezer that go to like -80F?

Properly built dry ice chest should hold dry ice for 2 to 3 weeks, please note dry ice isn't a dct or deep cryo treatment and it takes three days under the dry ice to see the difference depending on steel of course. AEB-L only needs to be dropped down to -95F and let it slowly warm up, it doesn't need to soak. I use dry ice on O1 as it definitely makes it tougher and I can temper it a point higher without the brittleness.

My friend Dtec did an experiment for me with a 440C blade. The blade was finished final HT and cryo and tempers all done. Dave left the knife all night in LN and measured to 4 x and got an increase of .9, almost a whole RC point. That is significant and a small temper would be needed afterwards, but on a finished knife the increase surprised us both.

Cryo can be kept simple or you can get complicated with it. It most definitely make blades better, and you can build an ice chest with 4" thick walls, but it has it's limits too. 3 days under dry ice will make most steels tougher as will overnight with LiqUid Nitrogen. LN also makes the little eta-carbides and will make the steel harder. As for snap tempers before subjecting the quenched metal to super cold temperature well I have been told it isn't necessary, but I would still do it to D2 as I've never had a failure with it. D2 is triple tempers with cryo in between, I get 59-61 hardness, 60 mostly and that is my target. Only ever cryoed it with dry ice.
.
Reply With Quote
  #12  
Old 03-14-2017, 10:54 PM
Blade-Runner Blade-Runner is offline
 
Join Date: Mar 2017
Location: North York
Posts: 2
So, it's a machine specifically designed for a completely controlled submersion in liquid nitrogen. However, it drops the temperature slow enough that there is no worries about thermal shock. It allows you to program your ramp rate and soak time.

https://www.nationalcryogenics.com/e...ll-new-ltk-27/

I have become fairly familiar with cryogenics since school, and have come to realize that there are quite a few misconceptions about how it is supposed to be performed. So I came to the forums to see how most other knife makers were doing it.

I have also read the following on Jay Fisher's website:

"What is the specific rate of cooling for most of these steels? 4-5 degrees Fahrenheit per minute. That means in order to reach -100F, it should take about 40 minutes (from room temperature), and to reach -325F should take about an hour and a half (from room temperature). This is why simply dipping blades into cryogenic baths of dry ice and alcohol or liquid nitrogen is a huge and destructive error, yet knifemakers who are uneducated in this process frequently do this, and tell others that it's the proper way to quench! Sad, truly sad for the knife client. The cryogenic process cooling rate is absolute and critical."

And I have yet to read anything that replaces a machine of this type. I am still in the learning curve, but I think it's an interesting concept.
Reply With Quote
Reply

Tags
440c, aeb-l, art, bee, blade, blades, build, building, cold, cryo, custom, custom knife, knife, knife making, knives, makers, making, quenched, simple, small, stainless, steel, temper


Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
 
Thread Tools
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is On

Forum Jump


All times are GMT -5. The time now is 11:14 PM.




KNIFENETWORK.COM
Copyright © 2000
CKK Industries, Inc. All Rights Reserved
Powered by ...

Powered by vBulletin® Version 3.8.4
Copyright ©2000 - 2017, Jelsoft Enterprises Ltd.
The Knife Network : All Rights Reserved