Blast media finishes

I bought glass beads for my new sandblaster.

I can't get the finish as dark as I would like.

Is there a general rule about blasting steel? Like the finer, more abrasive media gives the steel a darker color, while the larger gives a lighter color?

Or ????

Dave


__________________
Reply With Quote
  #2  
Old 12-20-2002, 09:33 AM
Geno's Avatar
Geno Geno is offline
RIP 11-09-2011
 
Join Date: Jun 2002
Location: Fort Worth, Texas
Posts: 1,606
Dave,
I don't blast my blades, but the grit wouldn't change the color(I don't think)
If you use a rougher grit and a dye, that would give you any amount of darkening desired.
I use a black laquer paint thinned(per batch) for consistancy, and brush it on, let it dry, then lightly sand, or wipe clean with laquer thinner. It leaves a dark background in the pits and darkens the blade as much as I want.(depending on how thick the black is)
This coating should be baked on too.
Do this before temper, and soak in the oven like a regular temper.
The paint becomes very hard and gives a protective coating on the blade too.
There are other solutions you might use too, this was just one idea.Black laquer is fairly common in damascus making to highlight contrast of steels and showing texture.
Reply With Quote
  #3  
Old 12-20-2002, 09:41 AM
Colin KC's Avatar
Colin KC Colin KC is offline
Master
 
Join Date: Jun 2002
Location: Kent, Europe
Posts: 775
Dave,
If you use glass beads, you'll get a satin type finish that is smooth(ish) to the touch & does appear quite light.

Aluminium oxide, or garnet, will give a rougher finish (easy to strike a match with a small movement) & what appears to be a darker finish (a couple of shades) this is due to the sharp profile of the surface as opposed to (with glass) a very wavy surface.

Using these more abrasive mediums will, however, work against any stain (read: rust) resistance your steel will have.


Hope this has been of some help


__________________
colin@britishblades.com
  • NT Freak'n Cow McIver
  • Knock, Knock
  • Who's There?
  • Cowsgo
  • Cowsgo Who?
  • NO, Cows Go Moo!
Reply With Quote
  #4  
Old 12-20-2002, 05:48 PM
wrathlord wrathlord is offline
Steel Addict
 
Join Date: Nov 2002
Posts: 151
I found it is the amount of alumina in the mix,and the size of bead,I notice the finer the micron the finer the finish,the gun and rate of blast is also important,smaller cabinets used to finish jewelery and stuff have much finer venturi's so the blast is more precise.The bigger industrial cabinets have guns usually and the finish with that is sandblast in a contained unit.The bead is much bigger and rougher.That is what I think your looking for.The beadblast is more of a flat grey coating,as opposed to the rough sandblast.
Reply With Quote
  #5  
Old 12-24-2002, 07:53 AM
Raymond Richard's Avatar
Raymond Richard Raymond Richard is offline
Hall of Famer
 
Join Date: Jun 2002
Location: Gresham, Oregon
Posts: 3,358
Dave, Haven't done any glass bead blasting for sometime but when I did I felt like I was spinning my wheels when starting off with glass bead. Found my results were so much better if I started with 150 grit garnet and then went with the glass bead. The glass beads pean and work much better is the surface is ruffed up with the 150 grit garnet first........


__________________
Raymond Richard
www.hawknknives.com

Reply With Quote
Reply


Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
 
Thread Tools
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is On

Forum Jump


All times are GMT -5. The time now is 11:27 AM.




KNIFENETWORK.COM
Copyright © 2000
? CKK Industries, Inc. ? All Rights Reserved
Powered by ...

Powered by vBulletin® Version 3.8.4
Copyright ©2000 - 2024, Jelsoft Enterprises Ltd.
The Knife Network : All Rights Reserved