HELP _ Im a dufus
OK- you may not me able to help my being a dufus....but I just left a 40cp SS blade in the temper oven overnight at 350deg.....I know.....
This was the second temper cycle, post cryo. Is it ruined? Can it be salvaged? Is everything OK ???? Please - some good news ?- __________________ Dennis "..good judgement comes from experience, experience comes from poor judgement.." -Gary McMahan, a cowboy poet and good dancer. http://www.facebook.com/home.php#!/p...24112090995576 |
#2
|
||||
|
||||
That shouldn't have done any harm, Dennis.
|
#3
|
||||
|
||||
WHEWW !! Glad to hear that Don. I was leaning that way but needed some assurance. Thank You!
__________________ Dennis "..good judgement comes from experience, experience comes from poor judgement.." -Gary McMahan, a cowboy poet and good dancer. http://www.facebook.com/home.php#!/p...24112090995576 |
#4
|
||||
|
||||
As long as you don't go above that you'll be fine.
You will expect a high energy bill next month, but the blade is OK. Geno |