  #1  
Old 03-15-2012, 11:16 PM
BItPlz BItPlz is offline
 
Join Date: Feb 2012
Location: Lincoln/Omaha Ne
Posts: 6
Pre HT Thickness

I am working to try a "flat grind" on one of my first blades, I have set up a make shift grinding station based on a Lansky Sharpening set that I have.
I am starting with 3/16" steel and I have read that you do not want to put an edge on the blade before HT as it could warp during quenching
My question is what thickness do I want to grind the blade edge down to before I attempt to Heat Treat it.
Reply With Quote
  #2  
Old 03-16-2012, 04:33 AM
Robert Mayo's Avatar
Robert Mayo Robert Mayo is offline
Skilled
 
Join Date: Nov 2005
Location: Renfrew Ont. in the heart of the Ottawa Valley
Posts: 676
I usualy leave the edge about the thickness of a dime to allow for decarb and finishing up after heat treating my carbon steel blades.

Bob
Reply With Quote
  #3  
Old 03-16-2012, 07:29 AM
Crex's Avatar
Crex Crex is offline
Moderator
 
Join Date: Sep 2002
Location: Acworth, GA and/or Hanging Dog, NC
Posts: 3,584
Putting an edge on your blade prior to HT won't be the cause of warpage. Warpage will occur due to unbalanced stresses in the steel and other factors such as uneven temps in quenchant, uneven heating, uneven.......key word. Get things even, remove all sharp angles "inner" and "outer" (these produce stress points during quench), and run a few normalizing cycles prior to quench (I prefer at least three), make sure your quenchant is at proper temp for your steel and you will greatly reduce the risk of warpage and stress cracks.
As Bob said the issue with preshaping/presharpening the edge too thin is primarily decarb.


__________________
Carl Rechsteiner, Bladesmith
Georgia Custom Knifemakers Guild, Charter Member
Knifemakers Guild, voting member
Registered Master Artist - GA Council for the Arts
C Rex Custom Knives

Blade Show Table 6-H
Reply With Quote
  #4  
Old 03-21-2012, 04:48 PM
Doug Lester Doug Lester is offline
Hall of Famer
 
Join Date: Sep 2006
Location: Decatur, IL
Posts: 2,612
I have had good luck with heat treating, rather re-heat treating, blades after I have put an edge on them. You do want to keep the austinization temperature down to just a bit above critical temperature to help prevent warping but that's really an overheating problem. Another reason to keep the edge just a tad thick is just safety. You might find out the hard way that sharp things cut. If you do have to work with a blade that has a sharp edge I would recommend that you tape it over. Blue painter's tape works well and it's easier to get off than regular masking tape.

Doug


__________________
If you're not making mistakes then you're not trying hard enough
Reply With Quote
Reply

Tags
blade, edge, grinding, heat treat, knife, sharpening, steel


Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
 
Thread Tools
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is On

Forum Jump

Similar Threads
Thread Thread Starter Forum Replies Last Post
A2 blade thickness ??? NJStricker The Newbies Arena 7 01-16-2006 07:26 AM
scales thickness Mungo Park The Newbies Arena 2 05-08-2005 07:40 PM
thickness chaos_customs The Newbies Arena 10 11-03-2004 01:20 PM
Edge Thickness Phantom23 The Newbies Arena 5 10-09-2003 06:53 AM
Thickness Tom Militano High-Performance Blades 2 10-02-2001 08:47 AM


All times are GMT -5. The time now is 03:20 PM.




KNIFENETWORK.COM
Copyright © 2000
? CKK Industries, Inc. ? All Rights Reserved
Powered by ...

Powered by vBulletin® Version 3.8.4
Copyright ©2000 - 2024, Jelsoft Enterprises Ltd.
The Knife Network : All Rights Reserved