  #1  
Old 08-10-2002, 07:33 AM
johnno johnno is offline
Registered
 
Join Date: Aug 2002
Location: australia
Posts: 9
Question hardening

I have a question about selective hardening, selective tempering ect . What in your opinion is better. Is it better to have a soft drawn spine or springy spine I have tried both and there are benefits to both methods but what is YOUR opinion, is clay coating better than drawing with a torch/forge.
I'm not trying to open a can of worms here but I'd like to here what other people think.
Reply With Quote
  #2  
Old 08-10-2002, 10:28 AM
Jerry Hossom Jerry Hossom is offline
Founding Member / Moderator
 
Join Date: Jun 2002
Location: Atlanta, GA
Posts: 411
I'm going to move this to Ed Caffrey's forum where I think you'll find more folks who can answer your questions.


__________________
Jerry Hossom
http://www.hossom.com

New Email Address: jerry@hossom.com
Reply With Quote
  #3  
Old 08-10-2002, 12:07 PM
Tom Ferry Tom Ferry is offline
Moderator
 
Join Date: Jun 2002
Location: Washington State
Posts: 147
Hi Johnno,
Well in my opinion how hard or soft the spine is all depends on the knives intended use and function and chance of warpage during the quench. I will fully harden my hunters unless I want to show a hamon or temperline. I normally seletive harden or edge quench my larger knives, not necessarily for aesthitics or for a soft tough back, although this can be a bonus, but more for less risk of warpage during the quench.
For example when I make a rope cutting competition knife I edge quench but do not temper the blade at the temp I would for a camp knife. I more or less stress relieve the blade, meaning the edge is about as hard as you can get away with without chipping under its intended use. If you used the same blade for chopping wood it would possibly break out. That doesnt mean its a bad heat treatment but the knife was heat treated for a specific task because the edge holding will go up a little which in competion can be crucial.
Currently I am mainly using clay and water quench for the 10xx series steels with great results but I still use oil for most of my damascus and either a full quench or an edge quench. I have never had much luck with the soft back draw with a torch personally but some do.
What you said about benefits of both heat treatments is right on and as an individual smith you must employ the technique you feel meets the needs of the overall package of that knife as each knife usually has a specific or intended use.
Have fun!


__________________
Tom Ferry/Bladesmith
Where Art Meets Performance


Reply With Quote
  #4  
Old 08-10-2002, 04:25 PM
johnno johnno is offline
Registered
 
Join Date: Aug 2002
Location: australia
Posts: 9
hardening

thanks tom I'm currently trying to make a rope cutting/skining knife. I forged the blade from 5160 triple quenched in 60
degrees C water and tempered to 350 F three times. I want to start making blades that will perform very well and pass a 90 degree bend test thats why I'm asking about harening styles. I have made a couple of D2 blades that met these tasks and passed very well but I want to learn more about different materials.
Thanks again for the help.
Reply With Quote
  #5  
Old 08-10-2002, 07:00 PM
Bob Warner's Avatar
Bob Warner Bob Warner is offline
Living Legend
 
Join Date: Jun 2002
Location: Royse City, Texas
Posts: 1,820
Go to Ed Caffery's site. He has step by step instructions on how to make a blade that will pass the journeyman test. Including answers to all of your questions.


__________________



Tumbling down the road at 35 MPH is no fun, TRUST ME!
Reply With Quote
  #6  
Old 01-18-2003, 04:09 PM
Gene Gene is offline
Banned
 
Join Date: Jul 2002
Location: Mayo, Florida
Posts: 184
Question hardening

Good day, Gentlemen:

I have a long blade, the cutting edge of which I would like to very precisely harden for 2' 1/2", but I was wondering if you have had any particular experience with:

INDUCTION HARDENING, where the sharp edge is placed inside an AC electrical coil, which energizes the steel and heats it up, depending on the frequency and amperage, for an extraordinarily precise edge hardening, or

Similarly, I would appreciate hearing from any of you who have had any experience with LASER BEAM HARDENING. A phosphate coating is applied over the sharp edge to facilitate absorption of the laser energy, and then the edge is quenched and tempered.

Or finally, have any of you tried any experiments with ELECTRON BEAM SELECTIVE EDGE HARDENING: Electron Beam Hardening is similar to laser beam hardening.

Thank you very much.

Gene
Reply With Quote
  #7  
Old 01-18-2003, 06:26 PM
jbgatlin jbgatlin is offline
Steel Addict
 
Join Date: Jun 2002
Location: Texarkana, AR
Posts: 106
Laser beams, eh?
Reply With Quote
  #8  
Old 01-18-2003, 07:22 PM
Gene Gene is offline
Banned
 
Join Date: Jul 2002
Location: Mayo, Florida
Posts: 184
Talking hardening

Yes, Sir.

A lot of the kit knives today are laser profiled, and there are companies which do selective hardening on knife blades by laser technology.

And I'm trying to learn more about it.

Thank you anyway.

Gene
Reply With Quote
  #9  
Old 01-18-2003, 07:28 PM
jbgatlin jbgatlin is offline
Steel Addict
 
Join Date: Jun 2002
Location: Texarkana, AR
Posts: 106
And all this time I have been using a torch! I need to get out more.
Reply With Quote
  #10  
Old 01-18-2003, 07:54 PM
Gene Gene is offline
Banned
 
Join Date: Jul 2002
Location: Mayo, Florida
Posts: 184
Talking hardening

Alas, JB, this particular blade is not quite that simple.

The blade is 24 3/4" x 2 1/2" x 3/8", 1084, and only 5/8" up from the sharp edge, I have to cut in an inlay channel, the entire length of the blade, and inlay it with twisted copper and brass wire. Thus, although the sharp edge needs to be hard, the blade needs to be soft enough, only 5/8" up, so that I can cut in the channel.

And, being a dumb, novice and old, I don't believe I am skillful enough to handle that.

Thank you, again, anyway.

Gene
Reply With Quote
  #11  
Old 01-19-2003, 01:35 AM
Tim Adlam's Avatar
Tim Adlam Tim Adlam is offline
Guru
 
Join Date: Jun 2002
Location: Oshkosh, WI USA
Posts: 1,486
..........0]
Reply With Quote
  #12  
Old 01-19-2003, 02:04 AM
whv whv is offline
Hall of Famer
 
Join Date: Jun 2002
Location: elgin or
Posts: 2,587
let us know how it turns ou for you, gene 0]


__________________
wayne
things get better with age ... i'm approaching magnificent
Reply With Quote
  #13  
Old 01-19-2003, 11:23 AM
Gene Gene is offline
Banned
 
Join Date: Jul 2002
Location: Mayo, Florida
Posts: 184
Talking

Good mornin', Wayne, from the Suwannee River!

Truthfully, I'm shootin' in the dark here.

To cut in that bottom inlay channel, only 5/8" from the sharp edge, I'd normally cut out the channel with a graver and chase hammer, but you can't do that if the steel there is hardened.

But it's a fairly wide channel - has to be large enough for two wires, twisted copper and brass - so just maybe it would be large enough for me to GRIND in the channel with a Dremel tool, and I plan to give that a try this morning, on a hardened junk blade.

But thank you for the encouragement, and yes I'll keep you posted.

Gene
Reply With Quote
  #14  
Old 01-27-2003, 11:26 AM
paul harm paul harm is offline
Master
 
Join Date: Aug 2002
Location: attica, mi.
Posts: 799
maybe i missed something, BUT- couldn't you cut the channel before the heat treat ? paul
Reply With Quote
  #15  
Old 01-27-2003, 11:39 AM
Gene Gene is offline
Banned
 
Join Date: Jul 2002
Location: Mayo, Florida
Posts: 184
Talking hardening

Good morning, Paul -

No, all the experts tell me you CAN'T first cut the inlay channels, then heat treat and temper the blade, and then come back and do the inlay. All the experts agree that the delicate little channels - with their almost microscopic edges - will be unusable after heat treating, because of the scaling, oxidation and such.

But thanks for the thought!

Gene
Reply With Quote
Reply

Tags
blade, forge, knife, knives


Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
 
Thread Tools
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is On

Forum Jump


All times are GMT -5. The time now is 02:39 AM.




KNIFENETWORK.COM
Copyright © 2000
? CKK Industries, Inc. ? All Rights Reserved
Powered by ...

Powered by vBulletin® Version 3.8.4
Copyright ©2000 - 2024, Jelsoft Enterprises Ltd.
The Knife Network : All Rights Reserved