So i'm finding that the steel i have here has been heat treated, but it's not very hard. I can file easily and can also scratch easily with a run of the mill hacksaw blade. Is there anything i can do aside from making a blade with it to know if it can produce a good blade? Any other testing I can do? I would really like to ship some to someone who has a lot of experience in blade making. Then they can let me know what we're dealing with here.
Thank You,
John
|