I'm using 01 Precision Ground, 5/32 thick. I've basically done everything you guys have mentioned except I do all my grinding prior to HT. I believe I'm leaving enough material to prevent warping.
The thing is, why has this never happened when I HT in my forge by simply bringing the blade up to non-magnetic then quenching?
I'm starting to wonder if I have a bad batch of steel. Could that be possible?
|