glad it worked! you may run into problems if it was hardened but not tempered for so long not gaurentee and I don't use d2 so cant promiss anything but I have heard that other have had problems with that in that steel....
how are you grinding the bevels and all that. IF you have a grinder just profile the blade NO bevels and HT it like that then grind the bevels after I do this on ALL of my blades and they don't warp at all maybe if you stirred it in the oil but I have never had a problem when I did it like that...
|