Ok so I haven't thrown my opinion because I have never worked with O1. All I have used is 1084, 440c, cpms35vn, and 154cm. I have never had a blade warp bad. Actually only 1 blade of 1084 ever had a slight warp witch was so slight I could grind it out, Maybe I have had a lot of luck maybe I shouldn't be talking about it don't want to jinx myself LOL Anyway I did just want to point out as ray said there are others than him that grind after heat treat. Well I am one of those others. All I do before HT is the profile that's it. As long as you keep dunking it in water and you will burn your hands before you blow the temper. Maybe this is one reason I haven't had blades warp on me there is more meat on the bone you know.
|