Assuming the warp is enough so you cant get rid of it when finish grinding, yes? If that's the case, I'd want to anneal and normalize the blade before attempting the heat treatment a second time. For carbon steel blades I've gone straight to re-heating, but an alloy like d2 I'd want to keep everything as by-the-book as possible
|